304 stainless steel sheet custom size export to Spain

304 Chemical compostion 

C: ≤ 0.08 Mn: ≤ 2.00 Si: ≤ 1.00 Cr: 18.0 ~ 20.0 Ni : 8.0 ~11.0 P: ≤ 0.045 S: ≤ 0.03 

304 Mechanical Properties

Hardness (HRB): ≤ 90

Tensile strength (Mpa): ≥ 520 

yield strength (Mpa): ≥ 205 

elongation %: ≥ 40 

density: 7.93

HL (hairLine finish) with Laser film, it's easy to do produce like lader cutting and bend




size model

Thickness: 0.3-3mm 

stainless steel  length:1000-6000 mm 

width;standard 1000 mm 1219 mm 1500 mm  

lenght and width can custom as request 


Finish model

Based finish:2B finish and NO.1 finish

Process finish based on 2B finish: NO.4,HL(hair line),6K,BA, mirror, Etch,Embossed

process finish also can do various colour: Golden,Rose Golden,Black and so on


Packing model

different finish with different packing

NO.1 finish:inside packed with kraft paper, outside with wooden pallet

2B finish : interlayer paper between each sheet, others same as NO.1

Process finish: stick with pvc on finish, others same as NO.1 


Transport model 

Normal ship,Track, train, small quantity with express and airplane

Corrosion Resistance :

* Resistance to corrosion in oxidizing environments is a result of the 18to 19% chromium that the 304 alloys contain

*resistance to moderately aggressive organic acids is a result of the 8 to 11% nickel that the 304 alloys contain

*at times,alloy 304L may show a lower corrosion rate than the higher carbon alloy 304,otherwise the 304,304L and 304H maybe considered to perform uniformly in most corrosive environment

*Alloy 304L is preferred for use in environments sufficiently corr0sive to cause intergranular corrosion of welds and heat-affected zones on susceptible alloys.

Heat Resistance :

*Good oxidation resistance in intermittent service to 1600°F and in continuous service to 1690°F

*Continuous use of 304 in the 800-1580°F range is not recommended if subsequent aqueous corrosion resistance is important

*Grade 304L is more resistant to carbide precipitation and can be heated into the above temperature range

Leave your suggestion and opinion to the product (Please fill out the information below.* indicates a required field.)

Product Name:
Your E-Mail: *
Content: *
Security Code: *